Per §3.3.2, which of the following salts in mixing water is described as 'completely destructive' to concrete strength?
A{'text': 'Sodium iodate', 'label': 'A'}
B{'text': 'Lead nitrate', 'label': 'B'}
C{'text': 'Zinc chloride', 'label': 'C'}
D{'text': 'Sodium carbonate', 'label': 'D'}
Answer & Solution
Correct answer: B. {'text': 'Lead nitrate', 'label': 'B'}
1. §3.3.2 reads: 'The effect of lead nitrate is completely destructive.'
2. Zinc chlorides retard set, sodium carbonate may cause quick setting, sodium iodate reduces initial strength — but none are described as completely destructive.
_Source: IGNOU ET-522 Block-1 Unit-3 Water, §3.3.2, p. 42_
Related questions
Per §3.4, sea water typically reduces the 28-day strength of concrete by the order of:Per §3.4, sea water is most strictly to be AVOIDED for use as mixing water in:Per §3.4, sea water has an average salinity of approximately:Per §3.3.5, an addition of approximately 0.20 percent sugar by weight of water in the mix Per Table 3.2, the recommended pH range of mixing water for concrete is:Per Table 3.2, the tolerable limit on TOTAL DISSOLVED SALTS in mixing water for concrete iPer §3.3.1, suspended particles in mixing water do NOT affect the strength of concrete up Per §3.3, the most reliable test for the suitability of a doubtful water for concrete is: